THE EFFECT OF ANNEALING TEMPERATURES AFTER THERMOMECHANICAL PROCESS TO THE CORROSION BEHAVIOR OF Ni3(Si,Ti) IN SULFATE SOLUTION

Gadang Priyotomo, Yasuyuki Kaneno


DOI: https://doi.org/10.12777/ijse.8.2.141-145

Abstract


The corrosion behaviour of the intermetallic compounds Ni3(Si,Ti) (L12: single phase), has been investigated using an immersion test, polarization method, scanning electron microscope in 0.5 kmol/m3 H2SO4 solution at 303 K.  Moreover, the corrosion behaviour of austenitic stainless steel type 304 was studied under the same experimental conditions as reference. It was found that the intergranular attack and uniform attack were observed on Ni3(Si,Ti) after thermomechanical and annealing processes (1173K and 1273K) respectively in the immersion test. From the immersion test and polarization curves, all annealed Ni3(Si,Ti) had less corrosion resistance compared to type 304. In addition, Ni3(Si,Ti) was difficult to form a stable passive film, but not for type 304.


Keywords


Intermetallic Compound; Immersion Test; Polarization Curve; Sulfate ion; Corrosion

Full Text:

FULL TEXT PDF

References


. Bunge. H. J, and Kohler. U (1996), Modeling Primary Recrystallization in fcc and bcc Metals by Oriented Nucleation and Growth with The Statistical Compromise Model, TEXTURES AND MICROSTRUCTURES, 28 : 231-259.

. Heller. H. W. F., Verbraak. C. A., and Kolster. B. H. (1984). Recrystallization at Grain Boundaries in Deformed Copper Bicrystals. ACTA METALLURGICA,32(9): 1395-1406.

. Kaneno, Y., and Takasugi.T. (2003). Grain-boundary character distribution in recrystallized L12 ordered intermetallic alloys. METALLURGICAL AND MATERIALS TRANSACTIONS A, 34A : 2429–2439.

. Kaneno,Y., Nakaaki, I., and Takasugi, T. (2002). Texture Evolution During Cold Rolling and Recrystallization of L12-type ordered Ni3(Si,Ti) Alloy, INTERMETALLICS,10 : 693-700.

. Oluyemi, D. O, Oluwole, O. I, and Adewuyi, B. O. (2011). Studies of the Properties of Heat Treated Rolled Medium Carbon Steel. MATERIALS RESEARCH 14(2): 135-141.

. Poliak, E. I., N. S. Pottore, R. M. Skolly, W. P. Umlauf, J. C. Brannbacka. (2009). Thermomechanical processing of advanced high strength in production hot strip rolling. LA METALLURGIA ITALIANA : 1–7.

. Priyotomo, G., Okitsu, K., Iwase, A., Kaneno, Y., Nishimura, R. and Takasugi, T. (2011). The corrosion behavior of intermetallic compounds Ni3(Si,Ti) and Ni3(Si,Ti) + 2Mo in acidic solutions. APPLIED SURFACE SCIENCE, 257(19): 8268-8274.

. Priyotomo, G., Wagle, S., Okitsu, K., Iwase, A., Kaneno, Y., Nishimura, R. and Takasugi, T. (2012). The corrosion behavior of Ni3(Si,Ti) intermetallic compounds with Al, Cr, and Mo in various acidic solutions. CORROSION SCIENCE, 60: 10-17.

. Priyotomo, G. (2013). Pitting Corrosion of Ni (Si,Ti) Intermetallic Compound at Various Chloride Concentrations. INTERNATIONAL JOURNAL OF SCIENCE AND ENGINEERING, 5(2): 25-28.

. Priyotomo.G.(2013), The Effect of Annealing Temperatures after Thermomechanical Process to The Corrosion Behavior of Ni3(Si,Ti) in Chloride Solution.TEKNOLOGI INDONESIA,36(2) : 97-104.

. Takasugi, T., Shindo, D., Izumi, O., and Hirabayashi, M. (1990). Metallographic and structural observations in the pseudo-binary section Ni3Si-Ni3Ti of the Ni-Si-Ti system. ACTA METALLURGICA ET MATERIALIA, 38: 739-745.

. Takasugi,T.(2000). Microstructural Control and Mechanical Properties of Nickel Silicides, INTERMETALLICS, 8 : 575-584.

. Takasugi, T., Nakayama, T. and Hanada, S. 1993a). Environmental embrittlement of Ni3(Si,Ti) single crystals. MATERIALS TRANSACTIONS JIM, 34(9):775-785.

. Takasugi, T., Hono, K., Suzuki, S., Hanada, S. and Sakurai, T. (1993b). Environmental embrittlement and grain boundary segregation of boron in Ni3(Si,Ti) and Co3Ti alloys. SCRIPTA METALLURGICA ET MATERIALA, 29(12): 1587-1591.

. Ushigami,Y. (2013). Theoretical Analysis and Computer Simulation of Secondary Recrystallization in Grain-oriented Silicon Steel. Nippon Steel Technical Report No.102 : 25-30.

. Wagle, S., Priyotomo, G., Kaneno, Y., Iwase, A., Takasugi, T. and Nishimura, R.(2011). Pitting Corrosion of Intermetallic Compound Ni3(Si,Ti) in Sodium Chloride Solutions. CORROSION SCIENCE, 53: 2514-2517.


Refbacks

  • There are currently no refbacks.


Published by Department of Chemical Engineering University of Diponegoro Semarang
Google Scholar

IJSE  by http://ejournal.undip.ac.id/index.php/ijse is licensed under Creative Commons Attribution 3.0 License.