STUDY OF CORROSION PERFORMANCE OF ZINC COATED STEEL IN SEAWATER ENVIRONMENT

*Ferry M  -  Department of Maritime Technology Universiti Malaysia Terengganu, Malaysia
Mohd Sukarnoor N.I.  -  Department of Maritime Technology Universiti Malaysia Terengganu, Malaysia

Citation Format:
Abstract

In this study, the corrosion protective mechanisms of zinc coating for mild steel in seawater were examined using weight  loss,  and  electrochemical impedance  spectroscopy  methods (EIS).  Coating is  a  technique to control the corrosion of a metal by providing an impervious metallic barrier by using sacrificial anode. The samples used in this study were fully zinc coated steel, zinc coated steel with scratch and mild steel as a control. Each sample undergoes the immersion process in seawater for 40 days. The results showed the corrosion rate of fully zinc coated steel decreases with immersion time from 0.03 mm/y to 0.01 mm/y and for zinc coated with scratch, from 0.034 mm/y to

0.012 mm/y. Impedance measurements studies revealed that fully zinc coated steel behave predominantly to be more practical anode in applying a great protection barrier for mild steel
Fulltext View|Download
Keywords: Coating, Mild steel, Seawater
Article Info
Section: Research Articles
Language : EN
Recent articles
Study On The Possibility Of Establishing Shipbuilding Cluster In Lampung Province Sumatra Indonesia As Pilot Project In Conjunction With Government’s Program On The Acceleration And Expansion Of Indonesian Economic Development (MP3EI) COMPARATIVE STUDY OF HYBRID CATAMARAN VERSUS DIESEL MONOHULL BOAT AS FERRY FOR SHORT DISTANCE ROUTES. STUDY OF CORROSION PERFORMANCE OF ZINC COATED STEEL IN SEAWATER ENVIRONMENT More recent articles
Most cited articles
MANEUVERING PERFORMANCE OF A FERRY AFFECTED BY RUDDER AREA AND SPEED COMPARATIVE STUDY OF HYBRID CATAMARAN VERSUS DIESEL MONOHULL BOAT AS FERRY FOR SHORT DISTANCE ROUTES. More cited articles

Last update:

No citation recorded.

Last update: 2024-11-25 06:58:39

No citation recorded.