@article{BFIS2706, author = {Masturi Masturi and Mikrajuddin Mikrajuddin and Khairurrijal Khairurrijal}, title = {Efektivitas Polyvinyl Acetate (PVAc) Sebagai Matriks Pada Komposit Sampah}, journal = {BERKALA FISIKA}, volume = {13}, number = {2}, year = {2012}, keywords = {}, abstract = { It was fabricated a composite using solid waste as filler and polyvinyl acetate (PVAc) as matrice. This work is as a solution of more serious solid waste problems. The solid waste used is paper waste and leaf one with their composition are 60% and 40% respectively. The crushed-solid waste then hot-pressed at 100 MPa of pressure and 150 ° C of temperature. Then, the compressive strength of composite before and after PVAc presence was investigated to get a composition in which the compressive strength is optimum. Keywords : composite, solid waste, polyvinyl acetate, compressive strength. }, pages = {61--66} url = {https://ejournal.undip.ac.id/index.php/berkala_fisika/article/view/2706} }
Refworks Citation Data :
It was fabricated a composite using solid waste as filler and polyvinyl acetate (PVAc) as matrice. This work is as a solution of more serious solid waste problems. The solid waste used is paper waste and leaf one with their composition are 60% and 40% respectively. The crushed-solid waste then hot-pressed at 100 MPa of pressure and 150°C of temperature. Then, the compressive strength of composite before and after PVAc presence was investigated to get a composition in which the compressive strength is optimum.
Last update:
Last update: 2024-11-21 03:29:17
Alamat Penerbit/Redaksi
Departemen FisikaFakultas Sains dan Matematika Universitas DiponegoroGedung Departemen Fisika Lt. I, Kampus FSM UNDIP Tembalang Semarang 50275Telp & Fax. (024) 76480822