PENGARUH PERBEDAAN SIFAT PENYANGGA ALUMINA TERHADAP SIFAT KATALIS HYDROTREATING BERBASIS NIKEL-MOLIBDENUM

Abstract

EFFECT OF ALUMINA SUPPORT PROPERTIES ON THE NICKEL-MOLIBDENUM BASE HYDROTREATING CATALYST. Effect of surface characteristics of three species of synthesized γ-alumina (alumina-1, alumina-2 and alumina-3) on characteristics NiMo catalysts has been studied. Those aluminas are derived from boehmite Catapal B by varying rasio mol nitric acid to boehmite. A sol-gel method is used to synthesize γ-Al₂O₃ support. The Nitrogen adsorption, X-ray diffraction (XRD), Temperature Programmed Reduction (TPR) of H₂, Temperature Programmed Desorption (TPD) of NH₃, and mechanical strength are used to characterize the supports and catalysts. The results showed that the surface area alumina affects the formation of crystalline MoO₃ in the NiMo catalyst, while γ-Al₂O₃-3 support which has the highest surface area (about 195 m²/g) compared to the other two types of alumina (>195 m²/g) does not have a crystalline MoO₃. The formation of crystalline MoO₃ is not influenced by the acidity alumina. Based on the results of XRD, it is  indicated that the supported alumina-3 NiMo catalyst (having the highest acid strength) shows that there is no presence of crystalline MoO₃. Pore size distribution of support did not change significantly after the deposition of Ni and Mo oxides. Mechanical strength of support also affects the strength NiMo catalyst. Support alumina-3 which has the highest mechanical strength gives the mechanical strength of the highest NiMo catalyst.

Pengaruh sifat penyangga γ-alumina hasil pengembangan (alumina-1, alumina-2 dan alumina-3) pada karakter katalis hydrotreating nikel-molibdenum (NiMo) telah dipelajari. Ketiga jenis γ-alumina diturunkan dari boehmite “Catapal B” dengan menvariasikan nisbah mol asam nitrat terhadap boehmite. Pembuatan γ-alumina menggunakan metoda sol-gel. Adsorpsi Nitrogen, X-ray difraksi (XRD), Temperature Programmed Reduction (TPR) H₂, Temperature Programmed Desorption (TPD) NH₃, dan kekuatan mekanik digunakan untuk mengkarakterisasi penyangga dan katalis. Hasil penelitian menunjukan bahwa luas permukaan alumina mempengaruhi pembentukan kristalin MoO₃ dalam katalis NiMo. Pada penyangga alumina-3 yang memiliki luas permukaan yang paling tinggi (sekitar 195 m²/g) di banding dua jenis alumina lainnya (>195 m²/g) tidak memiliki kristalin MoO₃. Pembentukan kristalin MoO₃ tidak dipengaruhi oleh sifat keasaman alumina. Berdasarkan hasil XRD ditunjukan bahwa pada katalis NiMo berpenyangga alumina-3 (memiliki kekuatan asam yang paling tinggi) tidak terdapat adanya kristalin MoO₃. Distribusi ukuran pori peyangga tidak berubah signifikan setelah deposisi oksida Ni dan Mo. Kekuatan mekanik penyangga mempengaruhi pula kekuatan katalis NiMo. Penyangga γ Al₂O₃-3 yang memiliki kekuatan mekanik yang paling tinggi memberikan kekuatan mekanik katalis NiMo yang tertinggi.