Transformation of Calcium Carbonate Polymorph From Various Type of Shells by Carbonation Methods

*Srie Muljani orcid scopus  -  Universitas Pembangunan Nasional "Veteran" Jawa Timur, Indonesia
Erwan Adi Saputra orcid scopus  -  Universitas Pembangunan Nasional "Veteran" Jawa Timur, Indonesia
Ketut Sumada  -  Universitas Pembangunan Nasional "Veteran" Jawa Timur, Indonesia
Open Access Copyright (c) 2021 Reaktor under

Citation Format:

The utilization of shells can reduce the accumulation of shell wastes and increase the value of shells to achieve ecological and economic incentives. This study examines the transformation of calcium carbonate polymorph from several types of shells to understand the causes of their characteristics in order to suitable for their use. The types of shells used in this experiment are selected based on consumable and their habitats such as snail shells, crab shells, eggshells, batik mussels shells, and golden conch shells. The prepared shells calcinate at 900 °C, the reaction with hydrochloric acid, and carbonation by flowing CO2 into a stirred reactor to produce precipitated CaCO3. The characteristics of polymorph CaCO3  in the sintering temperature of 30, 50, and 70 ℃ were identified by XRD, FTIR, and SEM morphological. The result is that the polymorphs formed from each shell are different in shape, size, and crystallinity. At the temperature of 70 ℃, the rhombohedral calcite was obtained from snail shells, the cubic calcite was obtained from batik mussel shell, while rhombohedral calcite multilayers obtained (100%) from golden conch shells. The aragonite was obtained from batik mussel shells at 30 and 70 ℃. The pure vaterite (100%) was obtained from snail shells and crab shells at 50 ℃. The characteristic of polymorph formed might be useful as information for more suitable applications, especially as nano-bio materials, optical, or filler

Note: This article has supplementary file(s).

Fulltext View|Download |  Research Instrument
Type Research Instrument
  Download (203KB)    Indexing metadata
 Research Instrument
Type Research Instrument
  Download (1MB)    Indexing metadata

Article Metrics:

Last update:

  1. A novel approach to mineral carbonation using deep eutectic solvents for the synthesis of nano-sized amorphous CaCO3

    Kyumin Jang, Dongwook Lee, Won Yong Choi, Jinwon Park, Yunsung Yoo. Separation and Purification Technology, 311 , 2023. doi: 10.1016/j.seppur.2023.123118

Last update: 2024-05-22 15:48:58

No citation recorded.